Qingdao Zhongxinhua Mei Plastic Co., Ltd. is a professional manufacturer of engineering plastic materials. You can order high-quality polyamide 6, paraformaldehyde, polycarbonate, polybutylene terephthalate and acrylonitrile butadiene styrene at favorable prices directly from our factory.
Advantages of carbon fiber reinforced nylon materials:
1. Joint venture with Chi Mei, strong factory, abundant supply, quality guaranteed.
2. Carbon fiber nylon: lightweight, wear-resistant, heat-resistant and aging-resistant.
3. High strength and high modulus: tensile strength 200, flexural strength 290, flexural modulus 11300.
4. MES system monitors the production process to ensure zero errors.
Wide application: used in aerospace/ unmanned aerial vehicles, automotive industry, sports and leisure, industrial manufacturing, electronic and electrical industries, etc., for making unmanned aerial vehicle frames/arms, automotive intake manifolds, bicycle parts, robot components, coil skeletons, etc.
| Physical properties table Flame retardant,heat resistant,impact resistant18 properties one-stop customization | |||||
| PHYSICAL PROPERTY TABLE | |||||
| Physical Property | Unit | Test Methods | FRPA6-1 | FRPA6-2 | GFFRPA6-1 |
| Tensile Strength | MPa | ISO 527-2 | 65 | 60 | 150 |
| Elongation at break | % | ISO 527-2 | 20 | 10 | 2 |
| Flexural Strength | MPa | ISO 178 | 80 | 105 | 225 |
| Flexural Module | MPa | ISO 179 | 2200 | 2800 | 9500 |
| Charpy Impact Strength | KJ/m² | ISO 179-1 | 7 | 5 | 11 |
| Density | g/cm³ | ISO 1183 | 1.27 | 1.17 | 1.58 |
| Vicat Softening Temperature | °C | ISO 306 | 195 | 200 | 215 |
| Shrinkage | % | ISO 294 | 1.2-1.5 | 0.8-1.2 | 0.2-0.6 |
| Flame retardancy | - | UL-94 | V-0 | V-0 | V-0 |
| Physical properties table Flame retardant,heat resistant,impact resistant18 properties one-stop customization | |||||
| PHYSICAL PROPERTY TABLE | |||||
| Physical Property | Unit | Test Methods | FRPA6-1 | FRPA6-2 | GFFRPA6-1 |
| Tensile Strength | MPa | ISO 527-2 | 65 | 60 | 150 |
| Elongation at break | % | ISO 527-2 | 20 | 10 | 2 |
| Flexural Strength | MPa | ISO 178 | 80 | 105 | 225 |
| Flexural Module | MPa | ISO 179 | 2200 | 2800 | 9500 |
| Charpy Impact Strength | KJ/m² | ISO 179-1 | 7 | 5 | 11 |
| Density | g/cm³ | ISO 1183 | 1.27 | 1.17 | 1.58 |
| Vicat Softening Temperature | °C | ISO 306 | 195 | 200 | 215 |
| Shrinkage | % | ISO 294 | 1.2-1.5 | 0.8-1.2 | 0.2-0.6 |
| Flame retardancy | - | UL-94 | V-0 | V-0 | V-0 |