Is PC-ABS stronger than ABS?
Qingdao Zhongxin Huamei’s Polycarbonate Alloy is a high-performance engineering plastic. Our Polycarbonate Alloy boasts superior strength, durability and processability, complying with RoHS & REACH standards. Ideal for automotive interiors and industrial parts, this Polycarbonate Alloy from our 1997-founded factory offers custom solutions—contact us now!
Flame Retardant PC/ABS V0 Flame Retardant Grade Virgin PC ABS Raw Material
CHIMEI JV · Source Factory | Free Samples | Flame-Retardant PCABS Customization
Performance Advantages：
1. Customizable Flame Ratings: Supports 1.5mm VA, 5VB, V0, V1, V2, HB (all customizable).
2. V0-Class Flame Retardancy: 1.5mm thickness meets standards, extinguishes immediately after removing from flame.
3. Halogen-Free & EU-Certified: Halogen-free flame-retardant formula, compliant with EU standard certifications.
Wide Applications
High-end equipment manufacturing, electronic & electrical products, automotive industry, office equipment, communication devices, lighting industry, safety protection & building materials, charging piles, printers, 5G base station equipment enclosures, etc.
Zhongxin Huamei's flame-retardant PC/ABS alloy material （pc/abs granules）meets the requirements in the Glow Wire Test at 750°C, while that of competitors （V0 Flame Retardant Grade Virgin PC ABS Raw Material）fails to do so in the same test at 750°C.
pc abs Flame Retardant alloy material Physical properties table Flame retardant,heat resistant,impact resistant18 properties one-stop customization | ||||
| AVERAGE GRADE | ||||
| ITEM | UNIT | TEST METHOD | TEST CONDITION | TEST RESULT |
| Density | g/cm³ | ISO 1183 | 23°C | 1.18 |
| Melt Flow Rate | g/10min | ISO 1133 | 260°C,2.16kg | 20 |
| Shrinkage | % | HM method | 23°C | 0.2-0.6 |
| Tensile Strength | MPa | ISO 527 | 50mm/min | 60 |
| Elongation at break | % | ISO 527 | 50mm/min | 80 |
| Flexural Strength | MPa | ISO 178 | 2.0mm/min | 90 |
| Flexural Module | MPa | ISO 178 | 2.0mm/min | 2500 |
| Heat Deflection Temperature | °C | ISO 75-2 | 1.8MPa | 82 |
| Vicat Softening Temperature | °C | ISO 306 | 50N | 100 |
| Charpy Impact Strength | KJ/m² | ISO 179 | 23°C | 45 |
| Izod Impact Strength | KJ/m² | ISO 180 | 23°C | 45 |
| Flame retardancy | Class | UL-94 | - | V0@1.6-3.0mm 5VA@3.2mm |
One of the standout features of premium pc abs flame retardant is its ability to handle stress. In comparative analyses against standard PC materials, the alloy demonstrates superior resilience.
In widely varied usage conditions, the residual stress in the molded part is significantly reduced. This improves resistance to stress cracking—a common headache in screw-fastened enclosures. At room temperature, the impact strength of this pc abs flame retardant is approximately 3 to 4 times that of standard PC materials.
For an injection molding factory, this means you can eject parts faster and assemble them with higher torque without worrying about the housing snapping. Using V0 Flame Retardant Grade Virgin PC ABS Raw Material ensures that the final appliance can withstand the rough handling of logistics and daily consumer use.
Conduct experimental tests on peers' benchmarked PC/ABS flame-retardant alloy material.
Articles about PC ABS Granules V0（V0 Flame Retardant Grade Virgin PC ABS Raw Materia）
lf you need more information about PC ABS Granules V0（V0 Flame Retardant Grade Virgin PC ABS Raw Materia）, please read these articles