Is PC-ABS stronger than ABS?
Qingdao Zhongxin Huamei’s Polycarbonate Alloy is a high-performance engineering plastic. Our Polycarbonate Alloy boasts superior strength, durability and processability, complying with RoHS & REACH standards. Ideal for automotive interiors and industrial parts, this Polycarbonate Alloy from our 1997-founded factory offers custom solutions—contact us now!
High temperature resistant PC/ABS
Performance Advantages:
1. Customizable Flame Ratings: Supports 1.5mm VA, 5VB, V0, V1, V2, HB (all customizable).
2. V0-Class Flame Retardancy: 1.5mm thickness meets standards, extinguishes immediately after removing from flame.
3. Halogen-Free & EU-Certified: Halogen-free flame-retardant formula, compliant with EU standard certifications.
Wide Applications
High-end equipment manufacturing, electronic & electrical products, automotive industry, office equipment, communication devices, lighting industry, safety protection & building materials, charging piles, printers, 5G base station equipment enclosures, etc.
| Physical properties table Flame retardant,heat resistant,impact resistant18 properties one-stop customization | ||||
| AVERAGE GRADE | ||||
| ITEM | UNIT | TEST METHOD | TEST CONDITION | TEST RESULT |
| Density | g/cm³ | ISO 1183 | 23°C | 1.18 |
| Melt Flow Rate | g/10min | ISO 1133 | 260°C,2.16kg | 20 |
| Shrinkage | % | HM method | 23°C | 0.2-0.6 |
| Tensile Strength | MPa | ISO 527 | 50mm/min | 60 |
| Elongation at break | % | ISO 527 | 50mm/min | 80 |
| Flexural Strength | MPa | ISO 178 | 2.0mm/min | 90 |
| Flexural Module | MPa | ISO 178 | 2.0mm/min | 2500 |
| Heat Deflection Temperature | °C | ISO 75-2 | 1.8MPa | 82 |
| Vicat Softening Temperature | °C | ISO 306 | 50N | 100 |
| Charpy Impact Strength | KJ/m² | ISO 179 | 23°C | 45 |
| Izod Impact Strength | KJ/m² | ISO 180 | 23°C | 45 |
| Flame retardancy | Class | UL-94 | - | V0@1.6-3.0mm 5VA@3.2mm |